Carbon Fiber (CF) reinforced resins—utilizing 10% to 40% carbon fibers in matrix polymers like PEEK, PA66, and PPS—represent the absolute pinnacle of metal-replacement plastics, offering an unrivaled strength-to-weight ratio, dimensional stability, and electrical conductivity (for ESD or EMI shielding). However, molding these composites introduces extreme abrasive wear on barrels, severe anisotropic shrinkage (warpage), and highly vulnerable weld lines where fibers fail to bridge. At Jucheng Precision, an ISO 9001 and IATF 16949 certified manufacturer, we resolve these issues with CPM powder metallurgy mold steels, scientific gate optimization, and pressurized high-temperature tooling. We provide a comprehensive, free DFM analysis within 24 hours to analyze fiber orientation, ensuring high-strength aerospace components verified by Zeiss CMM inspection.
열적 또는 화학적 안정성을 저하시키지 않으면서 하중 지지 구조 메커니즘에서 무거운 다이캐스트 아연 및 항공우주 등급 알루미늄 합금을 대체하기 위해, BASF의 Ultramid A3WC8은 40 wt.% 단탄소섬유 강화, 열안정화 폴리아미드 66(PA66-CF40) 매트릭스를 활용합니다. 밀도 1.28 g/cm³와 융점 262°C를 자랑하는 이 고성능 복합재는 23,500 MPa의 뛰어난 인장 탄성률과 고유한 정전기 방출(ESD) 특성을 제공합니다. IATF 16949 및 ISO 9001 인증 체계에서 운영되는 Jucheng Precision은 Ultramid A3WC8 성형을 전문으로 합니다. 5축 CNC 가공 S136 스테인리스 스틸 툴링의 지원을 받아 이방성 수축 변수(0.1%-0.4%)를 제어하여 Zeiss CMM으로 검증된 평평하고 구조적으로 결함 없는 부품을 제공합니다.
고하중 동적 메커니즘에서 무게를 추가하지 않고 구조용 알루미늄 및 아연 주조품을 대체하기 위해, Celanese의 Zytel 70C30HS(이전 DuPont)는 고급 30% 탄소 섬유 강화, 열안정화 폴리아미드 66(PA66-CF30) 매트릭스를 제공합니다. 1.28 g/cm³의 낮은 밀도와 262°C의 융점을 특징으로 하는 이 고성능 등급은 20,000 MPa의 탁월한 인장 계수와 함께 고유의 정전기 방전(ESD) 및 거의 제로에 가까운 마모를 제공합니다. IATF 16949 및 ISO 9001 인증 프레임워크 하에 운영되는 주성정밀은 Zytel 70C30HS 성형을 전문으로 합니다. 5축 CNC 가공 CPM 캐비티와 가압 금형 온도 컨트롤러의 지원을 받아, 우리는 이방성 수축 변수(0.1%-0.4%)를 제어하여 Zeiss CMM으로 검증된 평평하고 구조적으로 완벽한 부품을 제공합니다.
SABIC LNP THERMOCOMP EC006 is a PEI compound containing 30% carbon fiber with electrically conductive characteristics. The properties below reference SABIC Asia-region data with their test methods. Mechanical, electrical, dimensional and manufacturing requirements are reviewed for the actual component.
혹독한 산업 및 항공우주 환경에서 무게를 추가하지 않으면서 극한의 동적 내마모성, 기계적 강성 및 화학적 불활성을 유지하려면 최고급 구조 복합재가 필요하며, 시엔스코(Syensqo)의 라이톤(Ryton) CF30(구 솔베이)은 30% 탄소 섬유 강화 폴리페닐렌 설파이드(PPS) 매트릭스를 통해 이를 제공합니다. 최적화된 밀도 1.45 g/cm³와 열변형 온도(HDT) 265°C를 갖춘 이 고성능 등급은 21,000 MPa의 엄청난 인장 탄성률과 함께 고유의 정전기 방전(ESD) 특성을 제공합니다. IATF 16949 및 ISO 9001 프레임워크 하에 운영되는 주청 프리시전(Jucheng Precision)은 라이톤 CF30의 정밀 성형을 전문으로 합니다. 5축 CNC 가공된 S136 스테인리스 강 금형을 활용하여 이방성 수축 변수(0.1%-0.3%)를 제어하고 Zeiss CMM으로 검증된 동적 슬라이딩 부품을 제공합니다.
We process premium-grade carbon-fiber reinforced polymers (typically 10% to 40% CF load) designed for extreme weight reduction, metal-replacement, and ESD control:
| CF-Reinforced Class | 대표 브랜드 및 등급 | 주요 특성 및 장점 |
|---|---|---|
| PEEK-CF30 (High-Performance CF) |
• Victrex PEEK 450CA30 (30% CF) • Solvay KetaSpire KT-820 CF30 • Evonik Vestakeep 4000-CF30 |
Unmatched strength-to-weight ratio, continuous thermal resistance up to 260°C, and exceptional wear resistance. Perfectly replaces titanium and aluminum in aerospace brackets and oil seals. |
| PA66-CF30 (Engineering Nylon CF) |
• BASF Ultramid A3WC30 (30% CF) • Sabic LNP Thermocomp PA66 CF |
Extremely high flexural modulus and tensile strength (exceeding 200 MPa). Lighter than glass-filled alternatives. Excellent choice for UAV/drone arms, robotic joints, and racing sports gear. |
| PPS-CF30 (Semi-Crystalline CF) |
• Solvay Ryton CF30 (30% CF) • Toray Torcon CF grades |
Combines PPS’s complete chemical insolubility with carbon fiber’s low coefficient of thermal expansion (CLTE) and wear resistance. Suited for structural chemical valves and rotary seal wear rings. |
Because carbon fibers significantly restrict melt relaxation, advanced molding and tooling design are necessary:
| 성형 공정 | 공정 적합성 및 응용 |
|---|---|
| 표준 사출 성형 | Excellent. Configured with hardened PM-steel screws to mold lightweight structural brackets, heavy-duty gear sets, and aerospace connectors. |
| 인서트 성형 | Excellent. Highly utilized to encapsulate precision metal bushings and mounting studs, providing high torque resistance in ultra-rigid carbon-filled parts. |
| 정밀 마이크로 성형 | Good. Highly optimized for small, lightweight gears in advanced robotics and radiolucent micro surgical tool connectors. |
Carbon fibers are extremely abrasive and exhibit highly directional flow orientation. Managing mold wear and part warpage is a critical engineering challenge:
| Density (PA66-CF30) | 1.25 - 1.29 g/cm³ |
| Tensile Strength at Yield (PA66-CF30) | 210 - 275 MPa |
| 파단 시 인장 신율 | 1.5 - 2.5 % |
| Flexural Modulus (PA66-CF30) | 18,000 - 22,000 MPa |
| 아이조드 충격 강도 (노치, 23°C) | 70 - 110 J/m |
| 용융 온도 | 260 - 265 °C |
| 열변형 온도 (HDT @ 1.8 MPa) | 245 - 255 °C |
| 선형 몰드 수축률 (흐름 방향) | 0.05 - 0.15 % |
| 선형 몰드 수축률 (가로 방향) | 0.40 - 0.60 % |
| Surface Resistivity (Conductive Grade) | 1.0E+02 - 1.0E+06 Ohm/sq |
| 최대 부품 크기 | 800 x 600 mm |
| 최소 부품 크기 | 0.5 x 0.5 mm |