PBT-Sabic Valox 420
高電圧EVおよびアンダーフードの熱負荷下で高い機械的トルクと優れた寸法安定性を維持するには、重負荷複合材料が必要ですが、SABICのValox 420は、30%ガラス繊維強化ポリブチレンテレフタレートマトリックスを通じてそれを実現します。高い密度1.53 g/cm³と熱変形温度（HDT）207°Cを誇るこの半結晶性グレードは、電気モーター部品、スポットライトハウジング、重負荷コネクタ向けに世界的に指定されています。Jucheng Precisionは、IATF 16949およびISO 9001フレームワークの下で、Valox 420の成形を専門としています。50 HRCに硬化された5軸CNC機械加工S136工具鋼コアを利用し、異方性収縮（0.3%〜1.0%）を制御して反りを防ぎ、Zeiss CMMで検証されたバリのない構造部品を提供します。.
Valox 420 Mechanical Modulus & Thermal Tolerance Grid
VALOX™ Resin 420 is a 30% glass fiber reinforced, un-lubricated semi-crystalline PBT injection molding grade, certified to deliver outstanding strength, stiffness, and heat resistance under ASTM/ISO standards:
| Mechanical / Thermal Metric | Typical Value (ASTM/ISO) | Component Design Benefit |
|---|---|---|
| 破断引張強度 | 119 MPa (ASTM D638) | Provides immense structural load-bearing capacity, substituting die-cast metal brackets and casings with lighter weight. |
| 曲げ弾性率 | 7,580 MPa (ASTM D790) | Delivers high-stiffness, unbending structural integrity for electric motor casings, spotlights, and dynamic pump impellers. |
| 熱変形温度（HDT） | 207 °C (DAM @ 1.82 MPa) | Retains mechanical properties and shape under continuous thermal load in high-heat engine environments (HDT 215°C at 0.45 MPa). |
Heavy-Duty Process & Alignment Suitability for Valox 420
With its rapid crystallization and low melt viscosity of the base PBT, Valox 420 fills complex structural cavities consistently:
| 成形プロセス | Grade Adaptation & Engineering Focus |
|---|---|
| Precision Connector Assemblies | Excellent. Highly suitable for multi-pin automotive electrical blocks, sensor plugs, high-voltage terminals, and heavy-duty coil housings. |
| Electric Motor & Bobbin Components | Excellent. High tensile modulus prevents part deflection under tight copper winding tension on multi-slot bobbins and end bells. |
| Dynamic Spotlight Enclosures | Excellent. High continuous heat resistance and dimensional integrity are ideal for molding lighting reflectors, spotlight housings, and appliance handles. |
PBT-SABIC Valox 420 Tooling & Fiber Orientation Blueprint
Molding a 30% glass-fiber filled semi-crystalline resin like Valox 420 requires strict moisture control and optimized gating to prevent abrasive tool wear and warpage:
摩耗性工具摩耗の制御
30% short glass fibers act as an abrasive sanding medium under high injection speeds. Jucheng’s tooling division prevents cavity erosion by constructing molds with premium S136 stainless tool steel hardened to 48–52 HRC and machined on our 5-axis CNCs, ensuring long-term parting line precision.
Managing Anisotropic Shrinkage
Valox 420 shrinks much less along the flow (0.30%–0.50%) than perpendicular to it (0.40%–0.80%). We use Moldflow simulation during our free DFM review to balance gate locations, aligning glass fibers uniformly to prevent component warping and out-of-tolerance dimensions.
Key Application Fields for PBT-Sabic Valox 420
- 自動車パワートレイン＆ライティング（IATF 16949）： 高電圧EVバッテリーコネクタ、イグニッションコイルボビン、サーモスタットセンサーハウジング、ヘッドランプベゼルアセンブリ、および電動ウォーターポンプハウジング。.
- Electrical Components & Motors: Heavy-duty industrial relays, terminal blocks, electric motor end bells, smart-meter connector grids, and coil bobbins.
- Industrial Appliances & Lighting: 高負荷アプライアンスハンドル、屋外スポットライトハウジング、高温インジケーターベゼル、および構造用化学バルブハウジング。.
プロパティ
| 密度 | 1.53 g/cm³ |
| 破断引張強度 | 119 MPa |
| 引張破断伸び | 3.0 % |
| 曲げ強度 | 189 MPa |
| 曲げ弾性率 | 7,580 MPa |
| アイゾットノッチ付き衝撃強さ（23°C） | 85 J/m |
| Izod Unnotched Impact Strength (23°C) | 801 J/m |
| ロックウェル硬度（Rスケール） | 118 - |
| 融点 | 223 °C |
| 熱変形温度（HDT @ 0.45 MPa） | 215 °C |
| 熱変形温度（HDT @ 1.82 MPa） | 207 °C |
| 線形成形収縮率（流動方向） | 0.30 - 0.80 % |
| 線形金型収縮率（横方向） | 0.40 - 1.00 % |
| 体積抵抗率 | 3.2E+16 Ohm-cm |
| 最大部品サイズ | 1000 x 800 mm |
| 最小部品サイズ | 1 x 1 mm |