COP-Zeon Zeonor 1420R
Replacing optical glass and quartz in high-precision pre-filled syringes, diagnostic cuvettes, and microfluidic chips without introducing chemical extractables or leachables requires an ultra-pure amorphous polymer, which Zeon’s Zeonor 1420R Cyclic Olefin Polymer (COP) delivers. Featuring an extremely low density of 1.01 g/cm³ and a glass transition temperature (Tg) of 136°C, this USP Class VI and ISO 10993 certified resin provides 92% light transmittance, exceptionally low birefringence, and nearly non-existent water absorption (less than 0.01%). Jucheng Precision, under ISO 13485 certified medical frameworks, specializes in micro-molding Zeonor 1420R. Supported by certified ISO Class 7/8 cleanrooms and in-house 5-axis CNC-machined S136 stainless steel tooling, we guarantee zero-particulate contamination and pristine detail replication verified by Zeiss CMM.
Zeonor 1420R Optical Purity & Biocompatibility Profile
Zeonor® 1420R is an unreinforced amorphous Cyclic Olefin Polymer (COP) resin engineered by Zeon Corporation, certified to deliver outstanding optical clarity, extreme purity, and low water absorption under ISO/ASTM standards:
| Clinical Quality Factor | Zeonor 1420R Value | ميزة مكونات التكنولوجيا الطبية |
|---|---|---|
| Optical Transmittance | 92.0% Light Transmission & Low Birefringence | Delivers glass-matching transparency directly from polished core cavities, preventing light diffraction errors in analytical diagnostics. |
| Ultra-Low Extractables | معتمد وفق USP Class VI وISO 10993 | Highly purified amorphous matrix ensures zero toxic leachables, protecting sensitive pre-filled therapeutic drug storage. |
| الكارهة الشديدة للماء | Water Absorption Less Than 0.01% | Virtually non-hygroscopic. Excludes environmental moisture swelling, preventing micro-volume microfluidic channel errors. |
Precision Micro-Molding Configurations for COP Zeonor 1420R
With its high-flow melt index and amorphous stability, Zeonor 1420R processes consistently inside precision cavities:
| فئة عملية التشكيل | التوافق التشغيلي والتفاصيل التشغيلية |
|---|---|
| المختبر على رقاقة للموائع الدقيقة | Excellent. The primary process for Zeonor 1420R. Optimized for multi-cavity, ultra-thin-walled medical diagnostics and biochips down to 0.1mm channels. |
| Pre-filled Syringes & Vials | Excellent. High toughness, low outgassing, and excellent steam autoclaving resistance prevent dimensional distortion in medical syringes. |
| High-Fidelity Optical Lenses | Good. Outstanding dimensional stability, low outgassing, and ultra-low birefringence prevent structural warping in smart camera lenses. |
دليل الأدوات والمعالجة للغرف النظيفة ISO 13485
Molding an amorphous high-purity medical-grade polymer like Zeonor 1420R requires strict control of parting lines to prevent flash, alongside cleanroom contamination control:
قولبة الحقن في الغرف النظيفة من الفئة 7/8 ISO
Medical-grade COP resins must be protected from any airborne particulates or dust. Jucheng operates dedicated injection molding machines inside fully enclosed, positive-pressure ISO Class 7/8 cleanrooms. Raw material feeding, plastication, and robot part-ejection are completely automated and isolated.
أدوات S136 المصقولة بالمرآة (الحفاظ على النقاء)
لمنع تهيج الأنسجة من الخشونة الدقيقة السطحية المجهرية، نبني القوالب باستخدام الفولاذ المقاوم للصدأ عالي الكروم S136. يتم صقل التجاويف بدرجة عالية باستخدام معجون ألماس نظيف، مما يضمن أسطح أجزاء متوافقة حيويًا غير مسامية دون علامات سحب ديناميكية.
Low Birefringence & Thermal Stress Control
High melt shear during injection causes internal molding stresses, resulting in birefringence (rainbow refraction effects). Jucheng’s tooling division uses 5-axis CNC machines to cut precise runner geometries, applying slow, uniform packing pressures and keeping mold temperatures at 80°C–120°C (176°F to 248°F) using pressurized temperature controllers.
بروتوكول التجفيف الممتد باستخدام المجففات
Though COP absorbs minimal water, pre-drying raw material in clean-air desiccant hopper dryers at 110°C (230°F) for 4 hours is mandatory to prevent surface splay, dynamic micro-voids, and loss of transparent optical quality during high-speed runs.
Key Application Fields for COP-Zeon Zeonor 1420R
- Medical Diagnostics & Microfluidics (ISO 13485): رقائق التشخيص الدقيق عالية الكثافة، أجهزة التشخيص على الرقاقة، الكوفيتات، ألواح الفحص، وبراميل الحقن المعبأة مسبقاً.
- High-Fidelity Optical Lenses & Optics: العدسات البصرية الكروية واللا كروية، أغطية الكاميرا الواقية، أدلة الضوء، وألواح نشر الضوء.
- الأغلفة الإلكترونية عالية التقنية: أدراج حامل رقائق منخفضة ثابت العزل، تغليف مناولة أشباه الموصلات، وألواح نوافذ العرض الشفافة.
الخصائص
| الكثافة | 1.01 g/cm³ |
| Melt Mass-Flow Rate (MFR) (280°C/2.16kg) | 20 g/10 min |
| قوة الشد عند الخضوع | 65 MPa |
| استطالة الشد عند الكسر | 15 % |
| قوة الانحناء | 95 MPa |
| معامل الانحناء | 2,100 MPa |
| قوة تأثير إيزود المحززة (23 درجة مئوية) | 108 جول/م |
| نفاذية الضوء (3.0 مم) | 92 % |
| معامل الانكسار | 1.53 - |
| درجة حرارة الانتقال الزجاجي (Tg) | 136 °C |
| نقطة تليين فيكات (B/50) | 132 °م |
| درجة حرارة الانحراف الحراري (HDT @ 1.82 ميجا باسكال) | 123 °C |
| امتصاص الماء (تشبع عند 23 درجة مئوية) | <0.01 % |
| الانكماش الخطي للقالب | 0.6 % |
| الحد الأقصى لحجم الجزء (حد الغرفة النظيفة) | 600 × 400 مم |
| الحد الأدنى لحجم الجزء (حد قناة الموائع الدقيقة) | 0.1 × 0.1 مم |