Eliminating thermal quench distortion in large-scale mold blocks while securing superior core hardness uniformity over standard P20 requires an advanced nickel-alloy pre-hardened steel, which 718H (DIN 1.2738) mold steel delivers. Pre-hardened to a uniform 32–38 HRC, 718H steel contains nickel additives that ensure consistent hardness across thick tool sections up to 400mm depth, taking a fine SPI B-1 polish and crisp photo-etched textures. At Jucheng Precision, a certified ISO 9001 and IATF 16949 contract manufacturer, we specialize in 5-axis CNC machining of large 718 steel mold cavities. Delivering tool shot lives up to 500,000+ cycles, our 718 molds reliably process automotive panels and appliance enclosures, verified by Zeiss CMM inspection.
High-precision Aço para Molde 718 cavity manufacturing for large-scale appliance housings and automotive interior panels. Pre-hardened with nickel alloy addition to 32–38 HRC, 718H (DIN 1.2738) steel provides exceptional deep-section hardness uniformity and zero heat-treatment distortion across 500,000+ production cycles.
718H Mold Steel Metallurgical & Large Block Profile
718H is an upgraded nickel-chromium-molybdenum pre-hardened steel, engineered to maintain consistent hardness across thick mold core blocks:
| Metallurgical Parameter | 718 Steel Spec Metric | Large Tooling Advantage |
|---|---|---|
| Nickel-Alloy Pre-Hardening | 32 – 38 HRC (340 HB) | Pre-hardened at higher hardness than P20, offering superior resistance to core deformation under high injection pressures. |
| Deep Section Uniformity | DIN 1.2738 / AISI P20+Ni | Nickel additions prevent soft centers in thick steel blocks (up to 400mm depth), ensuring uniform 5-axis CNC cutter wear. |
| Texturização e Polibilidade | Compatível com SPI B-1 e Gravação Mold-Tech | Aceita texturas uniformes gravadas a ácido para acabamentos interiores automotivos e polimento de papel de alto brilho sem distorção do grão. |
Matriz de Compatibilidade e Aplicação de Polímeros com Aço 718
O aço pré-endurecido 718H é a referência do setor para componentes plásticos não corrosivos de médio a grande porte em Moldagem por Injeção de Plástico:
| Classe de Resina Polimérica | Material Base Recomendado | Estratégia de Ferramental 718 |
|---|---|---|
| Utensílios Domésticos de Grande Porte e Embalagens | Polipropileno (PP), Polietileno (PE), ABS, Poliestireno (PS) | Proporciona vida útil do molde de mais de 500.000 ciclos para caixas logísticas grandes, tampas traseiras de televisores e tanques de máquinas de lavar. |
| Acabamentos Interiores Automotivos e Para-choques | Policarbonato (PC), Poliamida (PA/Nylon), Ligas de PC/ABS | Suporta texturas de grão gravadas a ácido intrincadas para acabamentos de portas automotivas, porta-luvas e molduras de painéis. |
Engenharia de Ferramental em Aço para Moldes 718 e Projeto Pré-Endurecido
A moldagem com aço pré-endurecido 718H equilibra a velocidade de fabricação do molde com a precisão da cavidade através de quatro vantagens de engenharia:
Zero Heat-Treatment Distortion (35 HRC)
Because 718H steel is pre-hardened at the steel mill, no post-machining quench heat treatment is needed. This eliminates thermal stress distortion across large core plates, guaranteeing true-to-CAD dimensions on large appliance molds during Fabricação de Moldes Personalizados.
Deep-Section Uniform Hardness (Nickel Addition)
Unlike standard P20, 1% nickel addition in 718H prevents core softening in massive steel blocks. Jucheng’s 5-axis CNC machining centers cut deep cavity walls with uniform tool wear and ±0.005 mm accuracy.
Key Application Fields for 718 Steel Injection Molds
- Automotive Exterior & Interiors (IATF 16949): Large Ferramentas de Moldagem por Injeção de Produção tools for bumper fascia trims, door panels, glove boxes, and dashboard bezels.
- Large Consumer Appliances: Washing machine tubs, refrigerator door liners, television back enclosures, and air conditioner housings.
- Industrial Logistics & Commodities: Heavy-duty stackable crates, recycling bins, agricultural trays, and Moldagem por Injeção de Dois Componentes ou Moldagem por Injeção com Insertos hardware.
Propriedades
| Density (DIN 1.2738 / 718H Steel) | 7,85 g/cm³ |
| Faixa de Dureza (Pré-Endurecido) | 32 - 38 HRC |
| Dureza Brinell Equivalente | 340 HB |
| Resistência ao Escoamento por Tração | 920 MPa |
| Resistência à Tração Última | 1.100 MPa |
| Alongamento na Rutura | 18 % |
| Módulo de Flexão | 205 GPa |
| Condutividade Térmica (20°C) | 29,5 W/(m·K) |
| Coeficiente de Expansão Térmica (20-100°C) | 12.8 10⁻⁶/K |
| Capacidade de Superfície Polida SPI | SPI B-1 (Polimento Papel) - |
| Capacidade de Texturização | Compatível com Mold-Tech / VDI 3400 - |
| Vida Útil Garantida do Molde | 500.000+ Ciclos |
| Tamanho Máximo do Bloco da Cavidade do Molde | 2200 x 1600 mm |
| Tolerância Mínima de Usinagem | +/- 0.005 mm |